Jupiter-AAA铸铁焊条
Shield Metal Arc Welding(SMAW - Stick)
手工焊条电弧焊（SMAW-Stick）
For all cast irons - Meehanite, ductile, mealleable, gray cast irons and steel to cast iron.
适用于所有铸铁-Meehanite孕育铸铁、球墨铸铁、可锻铸铁、灰口铸铁，以及钢至铸铁的焊接。
Features
亮点
High Strength Up To 70,000psi/482MPa
抗拉强度高达70,000psi/482MPa
No Electrode Overheating
无焊条过热
Smooth Ductile Deposits
平滑韧性熔敷层
Steel To Cast Iron
钢和铸铁的焊接
More Efficient Deposits
更高效的熔敷
All Weldable Grades Of Cast Iron
所有可焊接等级的铸铁
Machinable Deposit
可加工熔敷层
Eliminates Porosity
无气孔
Characteristics
Jupiter AAA is engineered to give the user a high strength ductile weld without electrode overheating, thus producing a much more efficient deposit that is machinable. Welds are typically smooth, porosity free and flat. Excellent tie in between passes.
Jupiter AAA的设计目的是为用户提供高强度的韧性焊缝，而不会使焊条过热，从而更高效的产生可加工的熔敷层。焊缝通常光滑、无气孔且平整。出色的焊道间结合。
Jupiter AAA makes it easier and more cost effective to do large cast iron repairs. It can be used on dirty and oil impregnated pieces without the problem of electrode overheating. Superior choice for joining cast iron to steel.
Jupiter AAA使大型铸铁维修变得更容易、更具成本效益。它可以用于脏的和含油浸的工件，而不会出现焊条过热的问题。铸铁与钢连接的理想选择。
Technical技术参数
Size and Amps AC/DC+(DCEP)
|
Inches |
3/32 |
1/8 |
5/32 |
3/16 |
|
(mm) |
(2.4) |
(3.2) |
4.0 |
5.0 |
|
Amps |
65-90 |
70-130 |
100-175 |
200-275 |
Best Practices Application 应用
Remove cracks using grinder or Electra.
去除裂缝.
Stop drill cracks ends.
止裂孔。
Use medium arc and stringer beads.
使用中等弧长和线状焊道。
Skip weld, light peening recommended.
跳焊，建议轻敲击。
For critical or heavy parts preheat to 500?F(260?C).
对于关键或重型零件，预热至500?F(260?C)。
Cool slowly after welding. 焊后缓冷。