Jupiter A铸铁焊条
Shield Metal Arc Welding(SMAW - Stick)
For all Cast Iron - Meehanite,ductile, mealleable, gray cast irons and steel to cast iron.
适用于所有铸铁-Meehanite孕育铸铁、球墨铸铁、可锻铸铁、灰口铸铁和钢至铸铁的焊接。
Features
亮点
High Strength 79,000psi/545MPa
抗拉强度高达79,000psi/545MPa
Use On All Weldable Grades Of Cast Iron
用于所有可焊接等级的铸铁
All positions
全位置焊接
Welds Over Dirt and Oil
可以在油污上直接焊接
Eliminates Porosity
无气孔
Ideal For Cast Iron To Steel Joining
铸铁与钢连接的理想选择
Prevents Hard Spots
不会出现硬点
Easy To Use
易于使用
Machineable deposits
可加工熔敷层
Welds Over Slag
熔渣上的焊缝
Ductile Deposits
韧性熔敷层
No preheat required
不需要预热
Characteristics
特点
Jupiter-A has been engineered for the maintenance welder who must weld dirty, oil-soaked castings of unknown compositions. Sound, non-porous welds are produced without special preparation. Successful results are possible even when the joint is restrained.
Jupiter-A专为必须焊接成分未知的脏、浸油铸件的维护焊工设计。在无需特殊处理的情况下，即可产生完好、无孔的焊缝。即使接头受到约束，也有可能取得成功。
Jupiter-A makes it possible to repair machines and equipment in place without expensive tear down, thereby avoiding costly down time.
Jupiter-A可以在不需要拆卸的情况下将机器和设备维修到位，从而避免了高成本的停机时间。
Technical技术规格
Size and Amps AC/DC+(DCEP)
|
Inches |
3/32 |
1/8 |
5/32 |
|
(mm) |
(2.4) |
(3.2) |
(4.0) |
|
Amps |
48-72 |
80-120 |
100-150 |
Best Practices Application 应用
Remove cracks using grinder or Electra去除裂缝。
Stop drill crack ends.实施止裂孔。
Use medium arc and stringer beads. 使用中等弧度和线状焊道。
Skip weld and prevent overheating 跳焊并防止过热
Light peening recommended. 建议进行轻敲击。
For critical or heavy parts preheat to 500?F(260?C). 对于关键或重型零件，预热至500?F（260?C）。
Cool slowly after welding. 焊后缓冷。