Jupiter B TIG氩弧焊丝
Gas Tungsten Arc Welding(GTAW)
For cast irons and cast iron to steels. Joining and Build up. 用于铸铁以及铸铁和钢的焊接和堆焊。
Features 亮点
High Strength 60,000 psi/414MPa
抗拉强度高达60,000 psi/414MPa
High Nickel Content
镍含量高
Fully Machinable
完全可加工
Repairs Cracks
修复裂缝
Cast Iron to Steel Joints
铸铁-钢连接
Porosity Free Deposits
无孔隙熔敷物
Build Up Worn Areas
堆焊磨损区域
Easy To Use
易于使用
Characteristics 特点
Jupiter B TIG is a versatile inert arc filler metal specially suited for use on all cast iron parts or for joining cast iron to steel. Deposits are strong, dense and fully machinable. No special techniques are required for this easy to apply product. When repairing critical cast iron components such as valves, pumps, blocks or machine housings Jupiter B TIG assists the welder in producing high quality welds with minimum time and effort.
Jupiter B TIG是一种通用的铸铁氩弧焊丝，特别适用于所有铸铁零件的焊接或将铸铁与钢连接。熔敷物坚固、致密且完全可加工。易于使用，不需要特殊的技巧。在修理阀门、泵、缸体或机器外壳等关键铸铁部件时，Jupiter B TIG有助于焊工用最少的时间和精力生产出高质量的焊缝。
Technical技术规格
|
Inches |
1/16 |
3/32 |
1/8 |
|
(mm) |
(1.6) |
(2.4) |
(3.2) |
(AC with Hi-Frequency)
Best Practices Application 应用
Use DC straight polarity with argon. Adjust cup, tungsten and amperage to suit metal thickness.
使用氩气直流正接。调整保护罩，钨极以及电流以适应母材厚度。
Clean base metal. Remove all grease and other contamination from repair area.
清洁母材。
Remove sharp edges or protrusions in the base metal.
去除母材中的锋利边缘或突起。
For machinability or critical parts preheat to 500?F(260?C).
对于可加工性或关键零件，预热至500?F（260?C）。
Backstep to fill crater before withdrawing.
收弧前退焊以填满弧坑
Cool slowly after welding and light peening are recommended.
推荐焊后缓冷及轻敲击。