ER347Si不锈钢焊丝

材质

用途

化学成分

力学能力

线径（mm）

净重(kg)

阀芯直径(mm)

备注

ER304

主要用于焊接18Cr-8Ni钢

C:0.064%

Mn:1.65%

Si:0.42%

Ni:8.33%

Cr:17.10%

拉伸强度Mpa 1200

0.08-0.45

5/10/15/20

100/270/300

MIG:0.8-1.6

TIG:1.0-4.5

ER304L

主要用于焊接17Cr-8Ni钢

C:0.028%

Mn:1.65%

Si:0.42%

Ni:8.33%

Cr:17.10%

拉伸强度Mpa 1200

0.08-4.5

5/10/15/20

100/270/300

MIG:0.8-1.6

TIG:1.0-4.5

ER308

主要用于焊接19Cr-9Ni钢

C:0.064%

Mn:1.65%

Si:0.42%

Ni:10.33%

Cr:20.10%

拉伸强度Mpa 1200

0.08-4.5

5/10/15/20

100/270/300

MIG:0.8-1.6

TIG:1.0-4.5

ER308L

主要用于焊接20Cr-9Ni钢

C:0.024%

Mn:1.65%

Si:0.42%

Ni:10.33%

Cr:20.10%

拉伸强度Mpa 1200

0.8-4.5

5/12.5/15/20

100/270/300

MIG:0.8-1.6

TIG:1.0-4.5

ER309

主要用于焊接20Cr-13Ni钢

C:0.064%

Mn:1.65%

Si:0.42%

Ni:14.33%

Cr:20.10%

拉伸强度Mpa 1200

0.08-4.5

5/10/15/20

100/270/300

MIG:0.8-1.6

TIG:1.0-4.5

ER309L

主要用于焊接20Cr-14Ni钢

C:0.024%

Mn:1.65%

Si:0.42%

Ni:14.33%

Cr:20.10%

拉伸强度Mpa 1200

0.08-4.5

5/10/15/20

100/270/300

MIG:0.8-1.6

TIG:1.0-4.5

ER309Lsi

主要用于焊接20Cr-14Ni钢

C:0.024%

Mn:1.65%

Si:1.02%

Ni:14.33%

Cr:20.10%

拉伸强度Mpa1200

0.08-4.5

5/10/15/20

100/270/300

MIG:0.8-1.6

TIG:1.0-4.5

ER321

主要用于焊接16Cr-7Ni钢

C:0.064%

Mn:1.65%

Si:0.42%

Ni:8.33%

Cr:17.10%Ti0.73

拉伸强度Mpa 1200

0.08-4.5

5/10/15/20

100/270/300

MIG:0.8-1.6

TIG:1.0-4.5

ER347

主要用于焊接16Cr-9Ni钢

C:0.064%

Mn:1.65%

Si:0.42%

Ni:9.33%

Cr:17.10%

（Ta+Nb）（10*C）-10

拉伸强度Mpa 1200

0.08-4.5

5/10/15/20

100/270/300 0

MIG:0.8-1.6

TIG:1.0-4.5

ER347L

主要用于焊接17Cr-9Ni钢

C:0.064%

Mn:1.65%

Si:0.42%

Ni:9.33%

Cr:17.10%

（Ta+Nb）（10*C）-10

拉伸强度Mpa 1200

0.08-4.5

5/10/15/20

100/270/300 0

MIG:0.8-1.6

TIG:1.0-4.5

ER316

主要用于焊接16Cr-9Ni钢

C:0.064%

Mn:1.65%

Si:0.42%

Ni:10.33%

Cr:17.10%

Mo2.03

拉伸强度Mpa 1200

0.08-4.5

5/10/15/20

100/270/300

MIG:0.8-1.6

TIG:1.0-4.5

ER316L

主要用于焊接17Cr-9Ni钢

C:0.064%

Mn:1.65%

Si:0.42%

Ni:10.33%

Cr:17.10%

Mo2.03

拉伸强度Mpa 1200

0.08-4.5

5/10/15/20

100/270/300

MIG:0.8-1.6

TIG:1.0-4.5

ER310

主要用于焊接24Cr-19Ni钢

C:0.064%

Mn:1.65%

Si:0.42%

Ni:20.33%

Cr:25.10%

拉伸强度Mpa 1200

0.08-4.5

5/10/15/20

100/270/300

MIG:0.8-1.6

TIG:1.0-4.5