阿维斯塔2205basic双相不锈钢焊条
适用于2205型双相不锈钢的焊接，冲击韧性优异,详细说明：E2209-15双相不锈钢焊条化学成分C 0.03 Si 0.5 Mn 1.2 Cr 23.5 Ni 9.0 FN 40(WRC-92) N 0.16 Mo 3.0 碱性双相不锈钢焊条.
|
品名 |
类别 |
AWS型号 |
元素化学成份百分比 |
|||||
|
C |
Si |
Mn |
Cr |
Ni |
Mo |
|||
|
不锈钢 焊条 |
308L/MVR |
E308L-17 |
0.02 |
0.8 |
1.0 |
20.0 |
10.5 |
|
|
308L/MVR |
E308L-15 |
0.03 |
0.2 |
1.7 |
20.0 |
10.0 |
|
|
|
308L/MVR |
E308L-16 |
0.03 |
0.3 |
1.5 |
20.0 |
10.0 |
|
|
|
308/308H |
E308H-17 |
0.06 |
0.7 |
1.1 |
20.0 |
10.0 |
|
|
|
347/MVNb |
E347-17 |
0.02 |
0.8 |
0.8 |
19.5 |
10.0 |
|
|
|
347/MVNb |
E347-15 |
0.06 |
0.2 |
1.7 |
19.5 |
10.0 |
|
|
|
316L/SKR |
E316L-17 |
0.02 |
0.8 |
1.1 |
18.5 |
12.0 |
2.8 |
|
|
316L/SKR |
E316L-15 |
0.03 |
0.2 |
1.7 |
18.5 |
12.0 |
2.8 |
|
|
316L/SKR |
E316L-16 |
0.02 |
0.3 |
1.4 |
19.0 |
12.0 |
2.8 |
|
|
316/316H |
E316H-17 |
0.06 |
0.8 |
1.0 |
19.0 |
12.0 |
2.8 |
|
|
318/SKNb |
E318-17 |
0.02 |
0.8 |
0.8 |
18.5 |
12.0 |
2.8 |
|
|
318/SKNb |
E318-15 |
0.04 |
0.2 |
2.1 |
18.5 |
12.5 |
2.7 |
|
|
317L/SNR |
E317L-17 |
0.02 |
0.7 |
0.9 |
19.0 |
13.0 |
3.7 |
|
|
2205 |
E2209-17 |
0.02 |
0.8 |
0.7 |
23.0 |
9.5 |
3.0 |
|
|
2205 |
E2209-15 |
0.02 |
0.5 |
0.8 |
23.0 |
9.5 |
3.0 |
|
|
904L |
E385-17 |
0.02 |
0.8 |
1.2 |
20.5 |
25.0 |
4.5 |
|
|
383 |
E383-17 |
0.02 |
0.9 |
0.9 |
27.0 |
32.0 |
3.7 |
|
|
P12-R |
EniCrMo-12 |
0.02 |
0.4 |
0.4 |
21.5 |
|
9.5 |
|
|
P625 |
EniCrMo-3 |
0.02 |
0.5 |
0.2 |
21.5 |
|
9.5 |
|
|
307 |
E307-17 |
0.07 |
0.8 |
4.0 |
20.0 |
10.5 |
0.8 |
|
|
309L |
E309L-15 |
0.03 |
0.2 |
1.9 |
24.0 |
13.0 |
|
|
|
P5 |
E309MoL-17 |
0.02 |
0.8 |
1.1 |
22.5 |
13.5 |
2.7 |
|
|
P5 |
E309MoL-15 |
0.03 |
0.2 |
2.0 |
22.5 |
13.0 |
2.7 |
|
|
P5 |
E309MoL-16 |
0.03 |
0.3 |
1.4 |
22.5 |
13.5 |
2.7 |
|
|
P7 |
E312-17 |
0.09 |
0.8 |
0.8 |
29.0 |
9.5 |
|
|
|
P10 |
ENiCrFe-3 |
0.02 |
0.4 |
6.5 |
16.0 |
|
|
|
|
309 |
E309-17 |
0.05 |
0.8 |
1.0 |
24.0 |
13.5 |
|
|
|
310 |
E310-17 |
0.10 |
0.5 |
2.1 |
26.0 |
21.0 |
|
|
|
310 |
E310-15 |
0.12 |
0.3 |
2.4 |
25.5 |
21.0 |
|
|